Specifications
FMS is a good high temperature resistance filter fabrics
FMS compound Needle Punched Felt
FMS is a good high temperature resistance filter fabrics, this fabrics mainly made by 5.5 micron diameter glass fiber blend with P84 (polyimide), aramid(Nomex), PPS (ryton) fiber, with the three dimensional cellular structure, low air resistance, especial blend with P84 which with leaf style fiber, can increase the filter surface (80%), so easy to collect the dust, increase the fiber cohesion, can accept the high wind speed (50% higher about 1~1.4m/min), and also with the properties of abrasion resistance. This kind of fabrics widely used in metallurgical plant, chemical plant, coal fired boiler, incinerator, cement plant for dust collector or smoke filtration in high temperature circumstance.
Application
Iron and steel industry
Chemical industry
Coal black
Building material
Electric power Industry.
Specification
Composition:P84/Glass fiber/PTFE
Weight (g/m2):800
Thickness (mm):2.5
Air permeability (L/m2/s):8-15
Tensile strength (N/5×20cm)
Warp≥3000
Weft≥3100
Tensile elongation (%)
Warp<10
Weft<15
Broken strength (Mpa/min):3.85
Working temperature(°C)≤250
Short time working temperature(°C)270
Anti-acid:Excellent
Anti-alkali:Excellent
Anti-abrasion:Excellent
The stability of water solution:Medial
Finishing treatment:PTFE treatment
FMS is a good high temperature resistance filter fabrics
FMS compound Needle Punched Felt
FMS is a good high temperature resistance filter fabrics, this fabrics mainly made by 5.5 micron diameter glass fiber blend with P84 (polyimide), aramid(Nomex), PPS (ryton) fiber, with the three dimensional cellular structure, low air resistance, especial blend with P84 which with leaf style fiber, can increase the filter surface (80%), so easy to collect the dust, increase the fiber cohesion, can accept the high wind speed (50% higher about 1~1.4m/min), and also with the properties of abrasion resistance. This kind of fabrics widely used in metallurgical plant, chemical plant, coal fired boiler, incinerator, cement plant for dust collector or smoke filtration in high temperature circumstance.
Application
Iron and steel industry
Chemical industry
Coal black
Building material
Electric power Industry.
Specification
Composition:P84/Glass fiber/PTFE
Weight (g/m2):800
Thickness (mm):2.5
Air permeability (L/m2/s):8-15
Tensile strength (N/5×20cm)
Warp≥3000
Weft≥3100
Tensile elongation (%)
Warp<10
Weft<15
Broken strength (Mpa/min):3.85
Working temperature(°C)≤250
Short time working temperature(°C)270
Anti-acid:Excellent
Anti-alkali:Excellent
Anti-abrasion:Excellent
The stability of water solution:Medial
Finishing treatment:PTFE treatment