DIN 30CrNiMo8 steel is a medium carbon alloy structural steel which contain nickel,chromium and molybdenum. It's with medium hardenability designed for heavy duty compoents. It is also known as it's resistance to variable loads and impacts. It could characterize by high elasticity and tensile strength reaching over 1560Mpa. This material is used for production of heavily loaded parts, shafts and drive axes, steering shafts, crankshafts of engine, crews and element exposed to temperatures in the power industy. But this material is not suitable for welding and ultimately require additional preheating.
Â
Equivalent
Equivalent Grades of 30CrNiMo8(1.6580) | ||||
Germany DIN,WNr |
France AFNOR |
Russia  GOST |
China GB |
 International ISO |
30CrNiMo8 |
30CND8Â |
 3KH3M3F |
30Cr2Ni2Mo |
31CrNiMo8 |
Â
Chemical Composition
Grade |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
30CrNiMo8 |
0.26-0.34 |
0.4 |
0.3-0.6 |
0.025 |
0.035 |
1.8-2.2 |
0.3-0.5 |
1.8-2.2 |
30NCD8 |
0.26-0.34 |
0.1-0.4 |
0.3-0.6 |
0.030 |
0.025 |
1.8-2.2 |
0.3-0.5 |
1.8-2.2 |
Â
Mechanical Properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
 Â
Overviews
Size |
Round |
Dia 30-1200mm |
Plate/Flat/Block |
Thickness 6mm- 500mm |
|
Width 20mm-1000mm | ||
Heat Treatment |
Normalized ;Â Annealed ;Â Quenched ;Â Tempered |
|
Surface  Condition |
Black; Peeled; Polished; Machined; Grinded; Turned; Milled |
|
Delivery Condition |
Forged; Hot rolled; Cold drawn |
|
Test |
Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. |
|
Payment Terms |
T/T;L/C;/Money gram/ Paypal |
|
Trade Terms |
FOB; CIF; C&F; etc.. |
|
Delivery Time |
30-45 days |
|
Application |
30CrNiMo8 used for production of heavily loaded parts, shafts and dirve axes, steering shafts, crankshaft of engine, crews and element exposed to temperatures in the power industry and so on. |
Â
Delivery condition
For hot forged bar, usually the delivery condition is hot forged, annealed/QT rough turned/Black surface.
For hot rolled bar, usually the delivery condition is hot rolled, annealed/QT, Black surface.
For hot forged plate, usually the delivery condition is hot forged, annealed/QT, milled surface.
For hot rolled plate, usually the delivery condition is hot rolled, annealed/QT, black surface.